Glasses in the system [50Li 2 O-xB 2 O 3 -(50-x)P 2 O 5 ] (10 < x < 27.5), have been prepared by the melt quenching technique. Density, molar volume, hardness and Ft-IR spectroscopy have been employed to study the role of B 2 O 3 on the structure of the glass network. The results of density and hardness showed that both increased as P 2 O 5 is replaced by B 2 O 5 [as y was increased from 0.2 up to 0.4 where (y = B 2 O 3 /(B 2 O 3 +P 2 O 5 ))]. After Y 0.4 both of them decreased. Infrared spectra reveal that with the replacement P-O-B bonds are present at very low B 2 O 3 content and their relative amount increased within the whole range of B 2 O 3 . BO 4 tetrahedral groups are predominant (~ 100%) up to 15 mole% B 2 O 3 . Then, the proportion of BO 3 units starts to appear.
Nassar, A., Nabhan, E., & Ramadan, A. (2016). STRUCTURAL STUDY OF SOME LITHIUM BOROPHOSPHATE GLASSES USING DENSITY, HARDNESS AND INFRARED SPECTROSCOPY. Al-Azhar Bulletin of Science, 27(Issue 2-B), 1-9. doi: 10.21608/absb.2016.43970
MLA
A. M. Nassar; E. Nabhan; Al-Sh. Ramadan. "STRUCTURAL STUDY OF SOME LITHIUM BOROPHOSPHATE GLASSES USING DENSITY, HARDNESS AND INFRARED SPECTROSCOPY". Al-Azhar Bulletin of Science, 27, Issue 2-B, 2016, 1-9. doi: 10.21608/absb.2016.43970
HARVARD
Nassar, A., Nabhan, E., Ramadan, A. (2016). 'STRUCTURAL STUDY OF SOME LITHIUM BOROPHOSPHATE GLASSES USING DENSITY, HARDNESS AND INFRARED SPECTROSCOPY', Al-Azhar Bulletin of Science, 27(Issue 2-B), pp. 1-9. doi: 10.21608/absb.2016.43970
VANCOUVER
Nassar, A., Nabhan, E., Ramadan, A. STRUCTURAL STUDY OF SOME LITHIUM BOROPHOSPHATE GLASSES USING DENSITY, HARDNESS AND INFRARED SPECTROSCOPY. Al-Azhar Bulletin of Science, 2016; 27(Issue 2-B): 1-9. doi: 10.21608/absb.2016.43970